Polymer sheet

Polyvinylchlorid

Glass transition temperature: 82°C

Polystyrene

Glass transition temperature: 100°C

Polymethylmetacrylate

Glas transitioning temperature: 105°C

Polyphenyleneoxide

Glas transitioning temperature: 210

Polyethylene

Melting temperature: 138/110 (HDPE/LDPE)

Glasstransitioning temperature: -110

Polypropylene

Melting temperature: 160°C

Glastransitioning temperature: -10

Polyoxymethylene

Melting temperature: 180

Glas transitioning temperature: -85

Polybuthylene Terephthalate

Melting temperature: 240

Glas Transition temperature: 20

Polyamide 6,6

Melting temperature: 265

Glas transition temperature: 50

Polyethylen Terephtalate

Melting temperature: 265

Glas transition Temperature: 70

Polytetrafluoroethylene

Melting Temperature: 330

Glas transition temperature: -150

Polycarbonate

Glas transition temperatur: 150

Polyether Sulfone

Glas transitioning temperature: 190

Glas transition temperature: 190

Polyphenylenesulfide

Melting temperature: 285

Glas transition temperature: 85

Polyamide-imide

Glas transitionning temperature: >290

Polyetheretherketone

Melting temperature: 334

Glass transitioning temperature: 143

left until and with ester group: Hydroxybenzoic Acid

after ester hydronaphtoic acid with naphtalin centerpiece

Melting -& Glas transitioning temperature: wide range

Poly (Para phenylene benzobisimidazole)

Decomposition temperature: >400

Poly (Para phenylene benzobisoxazole)

Decomposition temperature: >400

Poly (Para Phenylene Benzobisthiazole)

Decomposition temperature: >400

Polymide

Decomposition temperature: >400

Decomposition temperature: >400